Glass Ceramic Ingot
| Size | Weight | Density |
Flexable Strength |
Vickers Hardness |
| 12.5*10mm3 | 2.97~3.02 g | 2.48 g/cm3 | 400 Mpa |
560 Mpa |
For veneers, inlays, full crowns on anterior teeth, high inlays, full crowns on posterior teeth and other cases
Highlights
- Chemical stability and flexural strength
- Easy to sand and reduce wear on the grinding head
- You can design more complex restorations
Suggested Crystallization Curve
| Start | Temp Rate | Temp | Temp Holding | Press Holding | |
| Less than100g | 700°C | 50°C/min | 930°C | 15min | 3min |
| 100g to 200g | 700°C | 50°C/min | 930°C | 20min | 3min |
Color
Glass Ceramic Ingot
| Size | Weight | Density |
Flexable Strength |
Vickers Hardness |
| 12.5*10mm3 | 2.97~3.02 g | 2.48 g/cm3 | 400 Mpa |
560 Mpa |
For veneers, inlays, full crowns on anterior teeth, high inlays, full crowns on posterior teeth and other cases
Highlights
- Chemical stability and flexural strength
- Easy to sand and reduce wear on the grinding head
- You can design more complex restorations
Suggested Crystallization Curve
| Start | Temp Rate | Temp | Temp Holding | Press Holding | |
| Less than100g | 700°C | 50°C/min | 930°C | 15min | 3min |
| 100g to 200g | 700°C | 50°C/min | 930°C | 20min | 3min |